Preparation of Polylactic Acid Graft Polyvinyl Acetate Compatibilizers for 50/50 Starch/PLLA Blending
Abstract:
Polylactic acid-g-polyvinyl acetate (PLLA-g-PVAc) was used as a compatibilizer for 50/50 starch/PLLA blend. PLLA-g- PVAc with different mol% of PVAc contents were prepared by grafting PVAc onto PLLA backbone via free radical polymerization in solution process. Various conditions such as type and the amount of initiator, monomer concentration, polymerization time and temperature were studied. Results showed that the highest mol% of PVAc grafting (16 mol%) was achieved by conducting graft copolymerization in toluene at 110°C for 10 h using DCP as an initiator. Chemical structure of the PVAc grafted PLLA was confirmed by 1H NMR. Blending of modified starch and PLLA in the presence compatibilizer with different amounts and mol% PVAc was acquired using internal mixer at 160°C for 15 min. Effects of PVAc content and the amount of compatibilizer on mechanical properties of polymer blend were studied. Results revealed that tensile strength and tensile modulus of polymer blend with higher PVAc grafting content compatibilizer showed better properties than that of lower PVAc grafting content compatibilizer. The amount of compatibilizer was found optimized in the range of 0.5-1.0 Wt% depending on the mol% PVAc.
Digital Object Identifier (DOI):

References:

[1] M. Zuideveld, C. Gottschalk, H. Kropfinger, R. Thomann, M. Rusu, and H. Frey, "Miscibility and properties of linear poly(L-lactide)/branched poly(L-lactide) copolyester blends", Polymer, vol. 47, pp. 3740-3746, 2006.
[2] T. Ouchi, S. Ichimurs and Y. Ohya, "Synthesis of branched poly(lactide) using polyglycidol and thermal mechanical properties of its solution-cast film," Polymer, vol. 47, pp. 429-434, 2006.
[3] W. Chin-San, "Improving Polylactide/starch biocomposites by grafting polylactide with acrylic acid-characterization and biodegradability assessment", Macromol. Biosci., vol 5, pp. 352-361, 2005.
[4] Z. Jian-Feng and S. Xiuzhi, "Mechanical properties of poly(lactic acid)/starch composites compatibilized by maleic anhydride", Biomacromolecule, vol 5, pp. 1446-1451, 2004.
Vol:14 No:05 2020Vol:14 No:04 2020Vol:14 No:03 2020Vol:14 No:02 2020Vol:14 No:01 2020
Vol:13 No:12 2019Vol:13 No:11 2019Vol:13 No:10 2019Vol:13 No:09 2019Vol:13 No:08 2019Vol:13 No:07 2019Vol:13 No:06 2019Vol:13 No:05 2019Vol:13 No:04 2019Vol:13 No:03 2019Vol:13 No:02 2019Vol:13 No:01 2019
Vol:12 No:12 2018Vol:12 No:11 2018Vol:12 No:10 2018Vol:12 No:09 2018Vol:12 No:08 2018Vol:12 No:07 2018Vol:12 No:06 2018Vol:12 No:05 2018Vol:12 No:04 2018Vol:12 No:03 2018Vol:12 No:02 2018Vol:12 No:01 2018
Vol:11 No:12 2017Vol:11 No:11 2017Vol:11 No:10 2017Vol:11 No:09 2017Vol:11 No:08 2017Vol:11 No:07 2017Vol:11 No:06 2017Vol:11 No:05 2017Vol:11 No:04 2017Vol:11 No:03 2017Vol:11 No:02 2017Vol:11 No:01 2017
Vol:10 No:12 2016Vol:10 No:11 2016Vol:10 No:10 2016Vol:10 No:09 2016Vol:10 No:08 2016Vol:10 No:07 2016Vol:10 No:06 2016Vol:10 No:05 2016Vol:10 No:04 2016Vol:10 No:03 2016Vol:10 No:02 2016Vol:10 No:01 2016
Vol:9 No:12 2015Vol:9 No:11 2015Vol:9 No:10 2015Vol:9 No:09 2015Vol:9 No:08 2015Vol:9 No:07 2015Vol:9 No:06 2015Vol:9 No:05 2015Vol:9 No:04 2015Vol:9 No:03 2015Vol:9 No:02 2015Vol:9 No:01 2015
Vol:8 No:12 2014Vol:8 No:11 2014Vol:8 No:10 2014Vol:8 No:09 2014Vol:8 No:08 2014Vol:8 No:07 2014Vol:8 No:06 2014Vol:8 No:05 2014Vol:8 No:04 2014Vol:8 No:03 2014Vol:8 No:02 2014Vol:8 No:01 2014
Vol:7 No:12 2013Vol:7 No:11 2013Vol:7 No:10 2013Vol:7 No:09 2013Vol:7 No:08 2013Vol:7 No:07 2013Vol:7 No:06 2013Vol:7 No:05 2013Vol:7 No:04 2013Vol:7 No:03 2013Vol:7 No:02 2013Vol:7 No:01 2013
Vol:6 No:12 2012Vol:6 No:11 2012Vol:6 No:10 2012Vol:6 No:09 2012Vol:6 No:08 2012Vol:6 No:07 2012Vol:6 No:06 2012Vol:6 No:05 2012Vol:6 No:04 2012Vol:6 No:03 2012Vol:6 No:02 2012Vol:6 No:01 2012
Vol:5 No:12 2011Vol:5 No:11 2011Vol:5 No:10 2011Vol:5 No:09 2011Vol:5 No:08 2011Vol:5 No:07 2011Vol:5 No:06 2011Vol:5 No:05 2011Vol:5 No:04 2011Vol:5 No:03 2011Vol:5 No:02 2011Vol:5 No:01 2011
Vol:4 No:12 2010Vol:4 No:11 2010Vol:4 No:10 2010Vol:4 No:09 2010Vol:4 No:08 2010Vol:4 No:07 2010Vol:4 No:06 2010Vol:4 No:05 2010Vol:4 No:04 2010Vol:4 No:03 2010Vol:4 No:02 2010Vol:4 No:01 2010
Vol:3 No:12 2009Vol:3 No:11 2009Vol:3 No:10 2009Vol:3 No:09 2009Vol:3 No:08 2009Vol:3 No:07 2009Vol:3 No:06 2009Vol:3 No:05 2009Vol:3 No:04 2009Vol:3 No:03 2009Vol:3 No:02 2009Vol:3 No:01 2009
Vol:2 No:12 2008Vol:2 No:11 2008Vol:2 No:10 2008Vol:2 No:09 2008Vol:2 No:08 2008Vol:2 No:07 2008Vol:2 No:06 2008Vol:2 No:05 2008Vol:2 No:04 2008Vol:2 No:03 2008Vol:2 No:02 2008Vol:2 No:01 2008
Vol:1 No:12 2007Vol:1 No:11 2007Vol:1 No:10 2007Vol:1 No:09 2007Vol:1 No:08 2007Vol:1 No:07 2007Vol:1 No:06 2007Vol:1 No:05 2007Vol:1 No:04 2007Vol:1 No:03 2007Vol:1 No:02 2007Vol:1 No:01 2007